temperature -70 20 180 Shear strength twenty three twenty three twenty three 150°C aging time 100 300 500 103 Τ(mpa) 200 21.5 17 17 temperature -60 20 100 200 250 h(mpa) 35 twenty two 11 6 5.2 temperature -70 20 180 Shear strength twenty three twenty three twenty three 150°C aging time 100 300 500 103 Τ(mpa) 200 21.5 17 17 temperature -60 20 100 200 250 h(mpa) 35 twenty two 11 6 5.2 Food Grade Essential Oil,Cumin Oil,Garlic Oil,Black Pepper Oil Ji'An ZhongXiang Natural Plants Co.,Ltd. , https://www.jazxnaturaloils.com
Neoprene (54-1) 100 Zinc Oxide 5 Antioxidant D 2 Accelerator TMTD 1 Sulfur 0.5
Ethyl, Gasoline, Tert-butyl phenolic resin 100 Mgo 8
0.3mpa/170°C/2h.J Greater than 30mpa Suitable for metal bonding. 130°C/4h. For metal bonding
Formula XX FN303 Plastic Group: Adhesive Type Neoprene 100 ENO 4 Mgo 5 Antioxidant 2 Group B: Tert-butyl phenolic resin 100
Mgo 4 H2O 0.5-1 Toluene 650
20°C/150h, or 70°C/8h. Aluminium alloy/canvas=3mpa. Suitable for adhesive formulation of sails, fabrics, rubber and metal. 21st JOI adhesive nitrile phenolic graft copolymer 20 Phenolphthalein resin 7 Propyl Gallate 1.0 Ethyl Acetate 160°C/4h, J greater than 15mpa. Non-uniform tear strength greater than or equal to 35kg/cm
In the following 150 °C for the bonding of metal structural parts Formulation twenty-five 450 plastic General neoprene 80 Nitrile rubber -26 20 Eno:ngo:cao 10:4:2 4010 Antioxidant 1
Sodium acetate: Sulfur 0.5:0.5 Accelerator CE: Propyl gallate 0.5:1.5 Tert-butyl phenolic resin 40
60°C/2h. For plastics, rubber, etc. Adhesive Formula 18 Panda 303# Glue Group: Phenolic and polyisocyanate solution B Group: Neoprene solution for fabrics such as garments. Carpet and other repair and bonding formulations 19 SY-401 adhesive (88# glue)
Neoprene (54-1) 100 Zinc Oxide 5 Antioxidant D 2 Accelerator TMTD 1 Sulfur 0.5
Ethyl, Gasoline, Tert-butyl phenolic resin 100 Mgo 8
0.3mpa/170°C/2h.J Greater than 30mpa Suitable for metal bonding. 130°C/4h. For metal bonding
Formula XX FN303 Plastic Group: Adhesive Type Neoprene 100 ENO 4 Mgo 5 Antioxidant 2 Group B: Tert-butyl phenolic resin 100
Mgo 4 H2O 0.5-1 Toluene 650
20°C/150h, or 70°C/8h. Aluminium alloy/canvas=3mpa. Suitable for adhesive formulation of sails, fabrics, rubber and metal. 21st JOI adhesive nitrile phenolic graft copolymer 20 Phenolphthalein resin 7 Propyl Gallate 1.0 Ethyl Acetate 160°C/4h, J greater than 15mpa. Non-uniform tear strength greater than or equal to 35kg/cm
In the following 150 °C for the bonding of metal structural parts Formulation twenty-five 450 plastic General neoprene 80 Nitrile rubber -26 20 Eno:ngo:cao 10:4:2 4010 Antioxidant 1
Sodium acetate: Sulfur 0.5:0.5 Accelerator CE: Propyl gallate 0.5:1.5 Tert-butyl phenolic resin 40
60°C/2h. Used for wood plastic rubber bonding
Formula twenty-three XY-402 plastic (73#)
Tert-butyl phenolic resin 30 Benzene 900 Neoprene, nitrile compound 104 (Chloropolymer: Butyronitrile-26 50:50
Accelerator H:mgo; Sulfur 0.5:3:0.5)
1mpa/143°C/10, peel strength (N/cm), fine cloth greater than or equal to 150, for nitrile
General formula of phenolic resin adhesive (below)
Formula 19 SY-401 adhesive (88# glue)